Vol. 3, No. 3 (Summer 2017) 8-15   

Link: http://www.acerp.ir/Vol3/No3/2.pdf
 
Downloaded: 19   Viewed: 117

  Preparation and Characterization of High Specific Surface Area γ-Alumina Nanoparticles Via Sol-Gel Method
 
S. M. Siahpoosh, E. Salahi, F. Hesari and I. Mobasherpour
 
( Received: March 10, 2017 – Accepted: December 30, 2017 )
 
 

Abstract    In the present investigation, γ-alumina nanoparticles with particle sizes less than 10 nm, high specific surface area (351 m2/g), high pore volumes and relatively narrow pore sizes distribution was prepared via sol-gel method in presence of aluminum isopropoxide as an aluminum precursor, distilled water, acetic acid as hydrolysis rate controller and tert-butanol as solvent. They had meso and macro porosities which the most of pores are in cylindrical shape. The received powder was characterized by simultaneous thermal analysis (STA) method. The calcined γ-alumina nanoparticles were characterized using X-ray diffractometer (XRD), Field Emission Scanning Electron Microscopy (FESEM), Fourier Transform Infrared Spectroscopy (FTIR) and nitrogen adsorption-desorption techniques. This study revealed that the precursor and solvent types, weight ratios of reactants, calcination temperatures and times were important factors to preparation of γ-alumina with high surface area and well defined narrow pore size distribution for heavy metals adsorption.

 

Keywords    γ-Alumina, Nanoparticles, Sol-gel, Aluminum Isopropoxide, Textural properties

 